Micronised Organic Grains |
|
|
How to use
• For surface preparation before waterproofing mainly used with
WAC-99 & WPC-99 for crack filling.
• Due to it’s out standing beading effect coating with WAC-99 or WPC-99 a uniform tough hydrophobic, impermeable plastic film is developed on the surface.
• The Plastic film developed with MOG-99 and WAC-99 or WPC-99 is durable to chemical attack, abrasion, corrosion.
• Used in high performance concrete for high workability, very high early strength and long term durability.
• Acts as a very good heat insulator.
Physical Properties :
| (a) Physical State |
: |
Micronised powder |
| (b) Colour Apperance |
: |
Grey fine powder |
| (c) Odour |
: |
Odourless |
| (d) Bulk density |
: |
0.56gm./cc without compact
0.70gm./cc after compact |
| (e) Specific Gravity |
: |
5 |
|
 |
|
|
Chemical Properties :
| (i) Silica Sio2 |
: |
88% + 2% |
| (ii) Carbon |
: |
5% |
| (iii) Moisture |
: |
2.5% maximum |
| (iv) pH |
: |
8 |
| (v) Water soluble |
: |
6.4% |
|
|
| |
|
Method of application for surface preparation & Waterproofing
• • Surface for treatment must be thoroughly cleaned of all laitance, loose materials, oil, greases etc.
• First look for big and medium crack and repair as follows : Cut the crack to a V-groove shape, mix thoroughly one part of WAC-99,
one part of water and three part of MOG-99 by weight, push the prepared paste inside the V shape crack.
• Let it dry for 2 hours.
• Prepare brushable mortar on with WAC-99, Water and MOG-99 in 1:1:1 proportion by weight.
• Apply 1st coat of the mortar on the surface for treatment and again after 30 minutes apply 2nd coat.
• After 12 hours apply two coats of WPC-99 as per the norms within 40 minutes interval.
Area of Application
• Terrace
• Side Wall
• Stapping
Advantages :
• Flawless repairing
• Durable & tough film formation
• plastic film developed on the top
• Apply 1st coat of the mortar on the surface for treatment and again after 30 minutes apply 2nd coat.
• Good weathering characteristics
• Negligible water absorption
• Withstand hydrostatic pressure
• Not suscepetible to alkali degradation & resistance to high alkali, sulphates and salts
• Very low dust pick up
• Eco-friendly
• Economical
• High heat resistance.
Precaution :
• Store in a cool & dry place
|
|
| |
|